ExxonMobil™
C6LL 18031.17 (LL 6318.17)
C6 Linear Low Density Polyethylene
ExxonMobil™ C6LL 18031.17 resin is a narrow molecular weight hexene copolymer that offers excellent toughness, impact strength and environmental stress crack resistance. This single pellet offers a solution for applications that typically require a blend of LLDPE for easy processability and HDPE to retain desired physical properties.
- Supplier
-
Additive
Thermal Stabilizer: Yes
Applications
- Closures
- Commercial articles
- Housewares
- Kitchenwares
- Spouts
Form(s)
Pellets
Revision Date
10/13/2022
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Based On |
|
|---|---|---|---|
| Density | 0.931 g/cm³ |
0.931 g/cm³ | ASTM D1505 |
| Melt Index | 18 g/10 min |
18 g/10 min | ASTM D1238 |
Thermal
| Vicat Softening Temperature | 216 °F |
102 °C | ASTM D1525 |
| Peak Melting Temperature | 260 °F |
127 °C | ExxonMobil Method |
Molded Properties
| Tensile Strength at Yield | 2200 psi |
16 MPa | ExxonMobil Method |
| Elongation at Break | 440 % |
440 % | ASTM D638 |
| Flexural Modulus1% Secant 2% Secant |
90000 77000 psi psi |
620 530 MPa MPa | ASTM D790B |
| Environmental Stress-Crack ResistanceCondition B, 10% Igepal, F50 | 750 hr |
750 hr | ASTM D1693B |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.