ExxonMobil™
C6LL 6836.67 (LL 6407.67)
C6 Linear Low Density Polyethylene
ExxonMobil™ C6LL 6836.67 resin is a narrow molecular weight hexene copolymer designed for applications that require outstanding environmental stress crack resistance. This resin offers good processability with minimal warpage and outstanding toughness for cold temperature durability.
- Supplier
-
Additive
Thermal Stabilizer: Yes
Applications
• Caps and Closures
• Cargo handling boxes
• Large Lids
• Large Part HousewaresForm(s)
Pellets
Revision Date
06/11/2020
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Based On |
|
|---|---|---|---|
| Density | 0.936 g/cm³ |
0.936 g/cm³ | ASTM D1505 |
| Melt Index | 6.8 g/10 min |
6.8 g/10 min | ASTM D1238 |
| Peak Melting Temperature | 259 °F |
126 °C | ExxonMobil Method |
Thermal
| Vicat Softening Temperature | 228 °F |
109 °C | ExxonMobil Method |
Molded Properties
| Tensile Strength at Yield | 2600 psi |
18 MPa | ExxonMobil Method |
| Elongation at Break | 760 % |
760 % | ExxonMobil Method |
| Flexural Modulus1% Secant: Procedure B 2% Secant: Procedure B |
96000 82000 psi psi |
660 570 MPa MPa | ExxonMobil Method |
| Environmental Stress-Crack ResistanceCondition B, 10% Igepal, F50 | > 1000 hr |
> 1000 hr | ExxonMobil Method |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.