DOW
DOW™ 132I
Low Density Polyethylene
DOW™ 132I Low Density Polyethylene Resin is a barefoot resin for heavy duty film applications. Optimum gauge range: 2.0−6.0 mil. It is used in shrink film, shipping sacks, construction film and other gauge film applications.
- Supplier
-
Overview
- A barefoot resin for heavy duty film applications
- Optimum gauge range: 2.0−6.0 mil
- Used in shrink film, shipping sacks, construction film and other gauge film applications
- Complies with U.S. FDA 21 CFR 177.1520( c )2.2.
- Complies with Canadian HPFB No Objection (With Limitations)
- Complies with EU, No 10/2011
- Complies with U.S. FDA-DMF
- Consult the regulations for complete details.
Additive
Antiblock: No; Slip: No; Processing Aid: No
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Method |
|
|---|---|---|---|
| Density | 0.921 g/cm³ |
0.921 g/cm³ | ASTM D792 |
| Base Density | 0.921 g/cm³ |
0.921 g/cm³ | Dow Method |
| Melt Index (190°C/2.16kg) | 0.25 g/10 min |
0.25 g/10 min | ASTM D1238 |
Molded Properties
| Film Thickness — Tested | 2 mil |
51 μm | |
| Film Puncture Resistance (2.0 mil (51 μm)) | 69.0 ft·lb/in³ |
5.71 J/cm³ | Dow Method |
| Film Toughness | ASTM D882 | ||
| MD : 2.0 mil (51 μm) | 2610 ft·lb/in³ |
216 J/cm³ | |
| TD : 2.0 mil (51 μm) | 2560 ft·lb/in³ |
211 J/cm³ | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 2.0 mil (51 μm) | 1750 psi |
12.1 MPa | |
| TD : Yield, 2.0 mil (51 μm) | 1750 psi |
12.1 MPa | |
| MD : Break, 2.0 mil (51 μm) | 4610 psi |
31.8 MPa | |
| TD : Break, 2.0 mil (51 μm) | 4190 psi |
28.9 MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 2.0 mil (51 μm) | 470 % |
470 % | |
| TD : Break, 2.0 mil (51 μm) | 660 % |
660 % | |
| Dart Drop Impact (2.0 mil (51 μm)) | 190 g |
190 g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 2.0 mil (51 μm) | 300 g |
300 g | |
| TD : 2.0 mil (51 μm) | 180 g |
180 g |
Thermal
| Vicat Softening Temperature | 205 °F |
96.1 °C | ASTM D1525 |
| Melting Temperature (DSC) | 230 °F |
110 °C | Dow Method |
Optical
| Gloss (45°, 2.00 mil (50.8 μm)) | 50 |
50 | ASTM D2457 |
| Haze (2.00 mil (50.8 μm)) | 11.3 % |
11.3 % | ASTM D1003 |
Extrusion Notes
| Fabrication Conditions For Blown Film: | |||
|
|||
|
|||
|
|||
|
|||
|
|||
|
|||
|
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.