ExxonMobil™
Exceed™ HD 5504 (Paxon™ SP5504)
High Density Polyethylene
Exceed™ HD 5504 is a blow molding grade high density polyethylene copolymer. It provides an exceptional balance of stress crack resistance, stiffness and impact strength. These properties, coupled with excellent processability on both continuous and intermittent equipment, afford significant opportunities for lightweighting and/or greater use of post-consumer recycle (PCR).
- Supplier
-
Additive
Thermal Stabilizer: Yes
Applications
• Blow Molding
• Drainage Pipes
• Food Packaging
• Personal Care
• Sheet ExtrusionForm(s)
Pellets
Revision Date
04/14/2021
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Method |
|
|---|---|---|---|
| Density | 0.955 g/cm³ |
0.955 g/cm³ | ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 0.35 g/10 min |
0.35 g/10 min | ASTM D1238 |
| Peak Melting Temperature | 266 °F |
130 °C | ExxonMobil Method |
Thermal
| Vicat Softening Temperature | 255 °F |
124 °C | ASTM D1525 |
Molded Properties
| Tensile Strength at Yield | 4000 psi |
27 MPa | ASTM D638 |
| Flexural Modulus ‑1% Secant (0.050 in/min (1.3 mm/min)) |
180000 psi |
1200 MPa | ASTM D790 |
| Environmental Stress-Crack Resistance100% Igepal | 180 hr |
180 hr | ASTM D1693B |
| Durometer Hardness (Shore D, 15 sec) | 59 |
59 | ASTM D2240 |
Impact
| Charpy Notched Impact Strength-4°F (-20°C) 73°F (23°C |
2.6 3.9 ft·lb/in² ft·lb/in² |
5.4 8.2 kJ/m² kJ/m² | ISO 179/1eA |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.