ExxonMobil™
HD 5003 (Paxon™ AB50-003)
High Density Polyethylene
ExxonMobil™ HD 5003 is a high density blow molding copolymer grade. This resin has very good stress crack resistance combined with high impact strength and rigidity.
- Supplier
-
Additive
Thermal Stabilizer: Yes; Antistatic: No
Applications
• Food Packaging
• Household and Industrial chemical containers
• Pharmaceutical Packaging
• Thermoformed Parts
Form(s)
Pellets
Revision Date
08/21/2020
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Method |
|
|---|---|---|---|
| Density | 0.950 g/cm³ |
0.950 g/cm³ | ASTM D4883 |
| Melt Index (190°C/2.16 kg) | 0.25 g/10 min |
0.25 g/10 min | ASTM D1238 |
Thermal
| Deflection Temperature Under Load (DTUL) at 66psi — Unannealed |
156 °F |
69 °C | ASTM D648 |
| Vicat Softening Temperature | 257 °F |
125 °C | ASTM D1525 |
| Peak Melting Temperature | 268 °F |
131 °C | ExxonMobil Method |
| Crystallization Peak, Tc | 243 °F |
117 °C | ExxonMobil Method |
Molded Properties
| Tensile Strength at Yield | 3700 psi |
26 MPa | ASTM D638 |
| Flexural Modulus 1% Secant: 0.051 in/min (1.3 mm/min) 2% Secant |
130000 110000 psi psi |
920 770 MPa MPa | ASTM D790A ASTM D790 |
| Environmental Stress-Crack Resistance100% Igepal | 50 hr |
50 hr | ASTM D1693B |
| Durometer Hardness (Shore D, 15 sec) | 61 |
61 | ASTM D2240 |
Impact
| Charpy Notched Impact Strength-4°F (-20°C) 73°F (23°C) |
1.9 4.3 ft·lb/in2 ft·lb/in2 |
4.0 9.0 kJ/m2 kJ/m2 | ISO 179/1eA |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.