HD 5201 (HD 7960.13)
High Density Polyethylene
ExxonMobil™ HD 5201 is a high molecular weight high density polyethylene blown film resin. Films made from HD 5201 resin exhibit excellent impact and toughness properties, as well as high stiffness. HD 5201 resin is particularly recommended for films less than 0.5 mil in thickness.
- Supplier
-
Additive
Antiblock: No; Slip: No; Processing Aid: No; Thermal Stabilizer: Yes
Applications
• Blown Film
• Grocery Sacks
• Institutional Can Liners
• Merchandise Bags
• Produce Bags On A Roll
• Trash BagsForms
Pellets
Revision Date
04/01/2019
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Based On |
|
|---|---|---|---|
| Density | 0.952 g/cm³ |
0.952 g/cm³ | ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 0.060 g/10 min |
0.060 g/10 min | ASTM D1238 |
| High Load Melt Index (190°C/21.6 kg) | 9.3 g/10 min |
9.3 g/10 min | ASTM D1238 |
| Peak Melting Temperature | 266 °F |
130 °C | ExxonMobil Method |
Film Properties
| Tensile Strength at Yield MD | 5400 psi |
37 MPa | ASTM D882 |
| Tensile Strength at Yield TD | 4700 psi |
32 MPa | ASTM D882 |
| Tensile Strength at Break MD | 13000 psi |
90 MPa | ASTM D882 |
| Tensile Strength at Break TD | 10000 psi |
70 MPa | ASTM D882 |
| Elongation at Break MD | 290 % |
290 % | ASTM D882 |
| Elongation at Break TD | 390 % |
390 % | ASTM D882 |
| Secant Modulus MD — 1% Secant | 150000 psi |
1000 MPa | ASTM D882 |
| Secant Modulus TD — 1% Secant | 160000 psi |
1100 MPa | ASTM D882 |
| Dart Drop Impact | 320 g |
320 g | ASTM D1709A |
| Elmendorf Tear Strength MD | 7 g |
7 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 40 g |
40 g | ASTM D1922 |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.