ExxonMobil™
HD 52140 (HD 6714.17)
High Density Polyethylene
ExxonMobil™ HD 52140 is a narrow molecular weight hexene copolymer designed for a wide range of injection molding applications requiring easy processability and good toughness properties. This resin is ideally suited for articles requiring low warpage, glossy surfaces and good cold temperature impact performance.
- Supplier
-
Additive
Antioxidant
Applications
• Bins
• Closures and Dispensers
• Food Packaging Containers
• Housewares
• Protective CapsRevision Date
06/22/2015
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Based On |
|
|---|---|---|---|
| Density | 0.952 g/cm³ |
0.952 g/cm³ | ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 14 g/10 min |
14 g/10 min | ASTM D1238 |
Thermal
| Deflection Temperature Under Load (DTUL) at 66psi — Unannealed | 160 °F |
71 °C | ASTM D648 |
| Deflection Temperature Under Load (DTUL) at 264psi — Unannealed | 113 °F |
45 °C | ASTM D648 |
| Peak Melting Temperature | 264 °C |
129 °F | ASTM D3418 |
Molded Properties
| Tensile Strength at Yield | 3600 psi |
25 MPa | ASTM D638 |
| Elongation at Yield | 250 % |
250 % | ExxonMobil Method |
| Flexural Modulus1% Secant 2% Secant |
180000 160000 psi psi |
1200 1100 MPa MPa | ASTM D790B |
| Environmental Stress-Crack Resistance10% Igepal, F50 | 3 hr |
3 hr | ASTM D1693B |
Impact
| Impact StrengthNotched Izod Impact (-40°F (-40°C)) | 0.77 ft·lb/in |
41 J/m | ASTM D256 |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.