ExxonMobil™
HD 5403 (Paxon™ AL55-003)
High Density Polyethylene
ExxonMobil™ HD 5403 is a high density polyethylene blow molding grade offering a good combination of stiffness and stress crack resistance.
- Supplier
-
Additive
Thermal Stabilizer: Yes
Applications
• Drainage Pipes
• Food Packaging
• Household and Industrial chemical containers
• Pharmaceutical Packaging
• Thermoformed Parts
• Thin Gauge SheetForm(s)
Pellets
Revision Date
08/21/2020
Resin Properties
Typical Value (English) |
Typical Value (SI) |
Test Method |
|
|---|---|---|---|
| Density | 0.954 g/cm³ |
0.954 g/cm³ | ASTM D1505 |
| Melt Index (190°C/2.16 kg) | 0.30 g/10 min |
0.30 g/10 min | ASTM D1238 |
Thermal
| Deflection Temperature Under Load (DTUL) at 66psi — Unannealed |
167 °F |
75 °C | ASTM D648 |
| Vicat Softening Temperature | 261 °F |
127 °C | ASTM D1525 |
| Peak Melting Temperature | 268 °F |
131 °C | ExxonMobil Method |
| Crystallization Peak, Tc | 244 °F |
118 °C | ExxonMobil Method |
Molded Properties
| Tensile Strength at Yield | 4100 psi |
29 MPa | ASTM D638 |
| Tensile Strength at Break | ASTM D638 | ||
| 2.0 in/min (50 mm/min) | 2900 psi |
20 MPa | |
| Elongation at Yield | 9 % |
9 % | ASTM D638 |
| Flexural Modulus | |||
| 1% Secant : 0.051 in/min (1.3 mm/min) | 160000 psi |
1100 MPa | ASTM D790A |
| 2% Secant | 130000 psi |
910 MPa | ASTM D790 |
| Environmental Stress-Crack Resistance | ASTM D1693B | ||
| 100% Igepal | 30 hr |
30 hr | |
| Durometer Hardness (Shore D, 15 sec) | 63 |
63 | ASTM D2240 |
Impact
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| ‑4°F (-20°C) | 2.9 ft·lb/in² |
6.0 kJ/m² | |
| 73°F (23°C) | 4.8 ft·lb/in² |
10 kJ/m² |
Disclaimer
The information presented here was acquired by Quantum from the producer of the material. Quantum assumes no responsibility or liability for the accuracy of the information contained on this website. Please refer to the downloadable pdf data sheet provided directly by the producer.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.