Qplast™
QPI 040HI
Impact Copolymer Polypropylene
QPlast™ QPI 040HI is a high-crystallinity copolymer resin with exceptional stiffness and impact resistance, tailored for injection molding, extrusion, and thermoforming applications.
- Supplier
-
Applications
- Consumer Applications
- Industrial Applications
- Tool Box
- Crates
- Pallets
- Toys
Form(s)
Pellets
Physical
Typical Value (English) |
Typical Value (SI) |
Test Method |
|
|---|---|---|---|
| Melt Flow Rate (230°C/2.16 kg) | 4.0 g/10 min |
4.0 g/10 min | ASTM D1238 |
Mechanical
| Tensile Strength at Yield | 3600 psi |
25 MPa | ASTM D638 |
| Elongation at Yield | 5.3 % |
5.3 % | ASTM D638 |
| Flexural Modulus — 1% 0.051 in/min (1.3 mm/min) |
200000 psi |
1379 MPa | ASTM D790A |
| Flexural Modulus — 1% 0.51 in/min (13 mm/min) |
219000 psi |
1510 MPa | ASTM D790B |
| Flexural Modulus (0.079 in/min (2.0 mm/min)) |
198000 psi |
1360 MPa | ISO 178 |
Impact
| Notched Izod Impact at 73°F (23°C) | No Break |
No Break | ASTM D256A |
Thermal
| DTUL at 66psi — Unannealed | 223 °F |
106 °C |
Disclaimer
The information presented in this document is believed to be accurate as of the date of publication. However, it is provided for general informational purposes only. This document is intended to offer guidance on the safe handling, use, processing, storage, transportation, disposal, and release of the product. It does not imply any express or implied warranty or quality specification, including but not limited to warranties of merchantability or fitness for a particular purpose. Users are responsible for independently assessing whether the product is suitable for their intended use and ensuring that it can be used safely and in compliance with relevant laws and regulations.
Nota:
Esto es una traducción. Quantum no asume responsabilidad alguna por la exactitud de la traducción. Cualquier discrepancia o diferencia creada en la traducción no es vinculante y no tiene ningún efecto legal. Si surge alguna duda relacionada con la exactitud de la información contenida en la ficha técnica traducida, consulte la versión en ingles.